Ce 3+ /Ce 4+ -Doped ZrO 2 /CuO Nanocomposite for Enhanced Photocatalytic Degradation of Methylene Blue under Visible Light.

In recent years, photocatalysis has been used as an environmentally friendly method for the degradation of organic pigments in water. In this study, Ce³⁺/Ce⁴⁺-doped ZrO2/CuO as a mixed semiconductor oxide was successfully prepared by a one-step hydrothermal method. The Ce³⁺/Ce⁴⁺-doped ZrO2/CuO has shown high degradation efficiency of methylene blue (MB), and the maximum degradation percentage was observed to be 94.5% at 180 min under irradiation visible light. The photocatalytic activity increases significantly by doping Ce³⁺/Ce⁴⁺ in ZrO2/CuO for MB degradation. Ce³⁺/Ce⁴⁺ doping is shown to reduce the (e^-/h⁺) recombination rate and improve the charge transfer, leading to enhanced photocatalytic activity of materials. The materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), FTIR, EDS, BET and diffuse reflectance spectroscopy (DRS). [ABSTRACT FROM AUTHOR]

Copyright of Toxics is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)