The Success of Fabrication of Pure SmFe 2 Phase Film with Outstanding Perpendicular Magnetic Anisotropy.

This study used DC magnetron sputtering technology to fabricate Sm-Fe films and systematically investigated the phase transition behavior of Sm-Fe films with different Fe ratios. It was found that at higher Fe content, the films consisted of Sm2Fe17 or SmFe7 phases; as Fe content decreased, the films were mainly composed of SmFe3 or SmFe2 phases; at higher Sm content, the films primarily consisted of Sm phase. Sm is prone to volatilization at high temperatures, so Ta was used as a capping layer to effectively suppress Sm volatilization, successfully synthesizing pure SmFe2 phase films at a nearly 1:2 ratio. The magnetic properties and magnetostrictive behavior of the SmFe2 films were investigated, revealing that pure-phase SmFe2 films exhibit good perpendicular magnetic anisotropy and magnetostriction properties. The larger stress along the perpendicular-to-film direction, resulting from the absence of substrate-induced constraints, contributes to the excellent perpendicular magnetic anisotropy of the films. This study successfully synthesized pure-phase SmFe2 films and discovered a new method for fabricating perpendicularly anisotropic films. The research findings are of great significance for the efficient synthesis of desired films with high phase formation temperatures containing volatile elements. [ABSTRACT FROM AUTHOR]

Copyright of Materials (1996-1944) is the property of MDPI and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)