Thermodynamic modeling of the CaO-SiO2-CaCO3-H2O closed and open system at 25ºC ; Modelización termodinámica del sistema CaO-SiO2-CaCO3-H2O a 25 ºC, en sistema cerrado y abierto

This paper reports on a thermodynamic calculation-based study of the CaO-SiO2-CaCO3-H2O closed system at 25 °C, conducted to determine the range of carbonate ion concentrations at which each phase of the system is stable. Portlandite (CH) and the CSH gel were found to be stable for carbonate ion concentrations of less than or equal to 7.62 X 10-3 mM/kg and 1.62 x 10-2 mM/kg, respectively. The CSH gel was found to remain stable in the system at pH values ranging from 10.18 to 10.48. In the CaO-SiO2-H2O open system at 25 °C, likewise studied, with PCO2 held constant at atmospheric values, only hydrated silica (SH) and calcite were found to be stable. ; En este trabajo se estudia el sistema CaO-SiO2-CaCO3-H2O, cerrado y a 25 ºC a través de cálculos termodinámicos, y se determina el rango de concentración de ion carbonato en el que son estables cada una de las fases del sistema. Se concluye que la portlandita (CH) y el gel CSH son estables para concentraciones de ion carbonato iguales o inferiores a 7,62 X 10-3 niM/kg y 1,62 x 10-2 mM/kg respectivamente. El rango de pH en el que el gel CSH es estable en el sistema es 10,18-10,48. También se estudia el sistema CaO-SiO2-H2O a 25 °C, en sistema abierto a PCO2 constante e igual a la de dicho gas en la atmósfera, encontrando que solo la sílice hidratada (SH) y la calcita son estables en dicho sistema.